GENERAL INFORMATION
ZIRCAR Alumina-Silica Insulating Blanket Type RS-C Moldable is composed of long, high strength ceramic fibers, with an inorganic alumina binder/rigidizing agent. It is a wet blanket that is shipped rolled up and sealed in a plastic bag to preserve its moldability.
Type RS-C Moldable forms a strong, rigid, low density insulation for applications to
1260°C (2300°F). It is 100% inorganic, non-combustible and contains no toxic or hazardous materials. Type
RS-C Moldable is ideal for insulation of complex shapes and exhibits excellent erosion resistance under conditions of high, hot gas velocity. It can be cut to any size with a knife, scissors, or steel rule die. It can be formed to virtually any shape desired. Type
RS-C Moldable possesses excellent strength for ease of installation. An unique process of locking in the binder ensures that it will not migrate. The result is a uniform homogeneous structure throughout the entire material.
Type RS-C Moldable does not adhere to itself, yet it can be cemented using air-set mortar. Type
RS-C Moldable will normally air dry in 24 to 48 hours, with all the properties of a pre-fired insulation. Curing can be accomplished with a hot air gun or torch, or by immediate temperature exposure in the application.
Type RS-C Moldable can be put directly into high temperature ovens or furnaces.
Type RS-CH Moldable has all of the same
properties as RS-C but is rated for 1450°C (2642°F)
|
SUGGESTED APPLICATIONS
Type RS- C Moldable is used as hot gas duct, stack and flue liners.
Type RS- C Moldable is used as custom molded valve enclosures.
Type RS- C Moldable is used as small appliance insulation.
Type RS- C Moldable is used as hot-face insulation where gas velocity is of concern.
Type RS- C Moldable is used for combustion chamber liners.
Type RS- C Moldable is used as back-up insulation for molten metal transport troughs.
Type RS- C Moldable is used for custom fabricated insulation parts.
Type RS- C Moldable is used as exhaust manifold insulation.
Type RS- C Moldable is used as back-up insulation.
Type RS- C Moldable is used as high temperature pipe insulation (internal and external).
Type RS- C Moldable is used as asbestos lagging replacement.
|
CHARACTERISTICS & PROPERTIES
Typical Composition, % |
|
Al2O3 |
66 |
SiO2 |
34 |
Other Metal Oxides |
0 |
Density, gm/cm3 (lb/ft3) |
.46 (29) |
Maximum Use Temp.*, C (F) |
1260 (2300) |
Color |
White |
Tensile Strength^, MPa (psi) |
.48 (70) |
Compressive Strength**, MPa (psi) |
|
@10% Compression |
0.2 (30) |
Shrinkage^, % |
|
Drying 75°C (167°F) |
0 |
Isothermal Soak, 24 hrs.@ 800°C (1472°F) |
2 |
Thermal Conductivity**,W/m K (BTU/ft2 °F /in) |
|
ASTM C177 |
|
200°C (392°F) |
0.06 (0.48) |
500°C (932°F) |
0.13 (0.91) |
800°C (1472°F) |
0.20 (1.42) |
AVAILABILITY
Item
# |
Description |
KS49 |
RS-C MOLDABLE, 24" X 60" X 1/8" |
KS50 |
RS-C MOLDABLE, 24" X 60" X 1/4" |
KS51 |
RS-C MOLDABLE, 24" X 60" X 1/2" |
KS52 |
RS-C MOLDABLE, 24" X 60" X 3/4" |
KS53 |
RS-C MOLDABLE, 24" X 60" X 1" |
KS60 |
RS-CH MOLDABLE, 24" X 60" X 1/4" |
KS61 |
RS-CH MOLDABLE, 24" X 60" X 1/2" |
KS62 |
RS-CH MOLDABLE, 24" X 60" X 1" |
PRICES ARE SUBJECT TO CHANGE WITHOUT NOTIFICATION
AND ARE SUBJECT TO ZIRCAR REFRACTORY COMPOSITES, INC. TERMS AND CONDITIONS. ALL
PRICES ARE F.O.B. FLORIDA, NY AND ARE IN U.S. DOLLARS
HOME
ZIRCAR REFRACTORY COMPOSITES, INC.
P.O. BOX 489
FLORIDA, NEW YORK 10921
TEL: 845-651-2200, FAX: 845-651-1515
email: sales@zircarchina.com
This information, which is subject to
change, is offered solely for your consideration and should not be taken as a
warranty or representation for which we assume legal responsibility. It is not
to be understood as permission or recommendation to practice a patented
invention without a license and the user should determine whether relevant
patents exist.
Copyrights and trademarks are the property
of ZIRCAR Refractory Composites, Inc.
{ for technical problems viewing these pages, please contact sales@zrci.com}
|